Garware Overhead Projection Transparency
film is a crystal clear polyester film, used as a presentation medium
on overhead projectors.
FEATURES:
- Crystal clear transparency
- Smooth and even surface
- High dimensional stability
- Uniform thickness and size
BENEFITS:
- Clear and sharp projection on overhead projector screen
- Good receptivity to various colours of marker pen inks
- Wrinkle free copies can be taken through copier machines
- Smooth and trouble free movement in printing machines which
accept film of specific thickness and size
APPLICATIONS:
- Marker pen writing
- Photocopying
- Book/Report binding
- Screen/Offset printing
THICKNESS: (micron)
USER PROFILE:
- Chief executive officers
- Senior management executives
- Marketing and advertising professionals
- Consultants
- Trainers
- Students of professional training institutes
- Architects
- Doctors
- Scientists and others
Garfilm - OHP - Transparency Film
| Sr.No.
|
Properties
|
Test
Method |
Unit |
Typical
Values
|
| General |
| 1 |
Thickness |
GPL
Method |
Micron |
75
|
100 |
125 |
175 |
| 2 |
Density |
ASTM-D-1505
|
gm/cc |
1.4 |
1.4 |
1.4 |
1.4 |
|
3
|
Water Absorption
|
ASTM-D 570
|
%
|
0.6
|
0.6
|
0.6
|
0.6
|
| Mechanical |
|
1
|
Tensile Strength at break
M.D / T.D
|
ASTM-D-882
|
Kg/cm2 |
1800
|
1800 |
1800 |
1800
|
| 2 |
Elongation
at break
M.D / T.D |
ASTM-D-882
|
%
|
130 |
130 |
130 |
130
|
| 3 |
Slip(COF)
Static
Dynamic |
ASTM-D-1894
|
- |
0.36
0.28 |
0.36
0.28 |
0.36
0.28 |
0.36
0.28 |
| Optical |
|
1
|
Haze
|
ASTM-D-1003
|
%
|
2
|
2 |
2 |
2 |
| Thermal |
|
1
|
Shrinkage at 150 oC for 30 Min.
|
ASTM-D-1204
|
|
|
|
|
|
| |
M.D. |
|
%
|
1.2 |
1.2 |
1.2 |
1.2 |
| |
T.D. |
|
%
|
0.4 |
0.4 |
0.4 |
0.4 |
| 2
|
Melting
Point |
DSC
|
oC |
255 |
255 |
255 |
255
|
| Availability |
|
|
Thickness(micron) |
Size (mm) |
No.
of sheets per packet |
| 1 |
75 |
210
x 297 |
100 |
|
2 |
100 |
210
x 297 |
100 |
|
3 |
100 |
210
x 297 |
20 |
|
4 |
100
|
254
x 305 |
100 |
| 5
|
125
|
210
x 297 |
100 |
| 6 |
175
|
210
x 297 |
50 |
M/Mic
- Micron
Max. - Maximum |
| |
|
The foregoing data have been obtained using standard test procedures
on defined specimens. The results should therefore only be regarded
as a general guide to material properties and not as design
data. |
| |
| FOR
SPECIFIC REQUIREMENTS WRITE TO US |
| |
|
|
 |
|