Sr.No.
|
Property
|
Unit
|
Test Method
|
Typical Values
|
| General |
|
1
|
Thickness
|
Micron
|
GPL Method
|
12
|
|
2
|
Yield
|
M2/Kg
|
GPL Method
|
59.4
|
|
3
|
Density
|
gm/cc
|
ASTM-D-1505
|
1.4
|
| Mechanical |
|
1
|
Tensile Strength at break ( MD )
|
Kg/cm2
|
ASTM-D-882
|
1700
|
|
2
|
Tensile Strength at break ( TD )
|
Kg/cm2
|
ASTM-D-882
|
2400
|
|
3
|
Tensile Strength at break
Diagonal at + 45° to MD
|
Kg/cm2
|
ASTM-D-882
|
1900
|
|
4
|
Tensile Strength at break
Diagonal at - 45° to MD
|
Kg/cm2
|
ASTM-D-882
|
2000
|
|
5
|
Elongation at break ( MD )
|
%
|
ASTM-D-882
|
150
|
|
6
|
Elongation at break ( TD )
|
%
|
ASTM-D-882
|
80
|
|
7
|
Elongation at break
Diagonal at + 45° to MD
|
%
|
ASTM-D-882
|
140
|
|
8
|
Elongation at break
Diagonal at - 45° to MD
|
%
|
ASTM-D-882
|
123
|
|
9
|
Slip(COF)
|
--
|
ASTM-D-1894
|
0.4
|
|
10
|
Ratio
=(F30-Fy)
/ C |
-- |
F30=Force
at 30%Elongation
Fy=Force at Yield
C=Constant of 0.054 |
<21 across full
web |
| Optical |
|
1
|
Haze
|
%
|
ASTM-D-1003
|
3.5
|
|
2
|
Total Luminous Transmission
|
%
|
ASTM-D-1003
|
86
|
| Thermal |
|
1
|
Shrinkage @ 150 ° C 30 min
|
|
ASTM D 1204
|
|
| |
MD
|
%
|
|
2
|
| |
TD
|
% |
|
1 |
|
2
|
Melting Point |
o C |
DSC
|
255 |
Garfilm ISP is an Isotropic film which is specially made for lidding applications.
Mechanical Properties of this film are such that the film exhibits higher elongation
in the direction of peel.