Sr.No.
|
Property
|
Unit
|
Test Method
|
Typical Values
|
| General |
|
1
|
Thickness
|
Micron
|
GPL Method
|
125
|
190
|
250
|
350
|
|
2
|
Yield
|
M2/Kg
|
GPL Method
|
5.71
|
3.76
|
2.86
|
2.04
|
|
3
|
Density
|
gm/cc
|
ASTM-D-1505
|
1.4
|
1.4
|
1.4
|
1.4
|
|
4
|
Water Absorption ( Max)
|
%
|
ASTM-D-570
|
0.6
|
0.6
|
0.6
|
0.6
|
|
5
|
Oligomer Extraction
|
%
|
GPL Method
|
1.5
|
1.5
|
1.5
|
1.5
|
| Mechanical |
|
1
|
Tensile Strength at break (MD/TD)
|
Kg/cm2 |
ASTM-D-882
|
1800
|
1800
|
1800
|
1600
|
|
2
|
Elongation ( MD / TD )
|
%
|
ASTM-D-882
|
150
|
150
|
150
|
150
|
|
3
|
Slip(COF)
|
--
|
ASTM-D-1894
|
0.3
|
0.3
|
0.3
|
0.3
|
| Optical |
|
1
|
Haze
|
%
|
ASTM-D-1003
|
70
|
80
|
88
|
94
|
| Thermal |
|
1
|
Shrinkage @ 150 ° C 30 min
|
|
ASTM-D-1204
|
|
|
|
|
| |
MD
|
%
|
|
1
|
1
|
1
|
1
|
| |
TD
|
%
|
|
0.4
|
0.4
|
0.4
|
0.4
|
|
2
|
Shrinkage @ 200oC 30 min
|
%
|
ASTM-D-1204
|
|
|
|
|
| |
MD ( Max )
TD ( Max ) |
%
%
|
|
7
7
|
7
7
|
7
7
|
7
7
|
|
3
|
Melting point
|
°C
|
DSC
|
255
|
255
|
255
|
255
|
|
4
|
Specific Heat @ 25 °C
|
cal/gm°C
|
|
0.32
|
|
5
|
Coeff of Thermal Expansion
between
20° C & 50 ° C
|
1/K(cm/cm °C)
1/K(cm/cm°C)
|
|
36 X 10-6(MD)
23 X 10-6(TD)
|
| Electrical |
|
1
|
Break Down Voltage
( on 2" Brass electrod )
|
KV
|
ASTM-D-149
|
15.5
|
18.0
|
19.5
|
22.5
|
|
2
|
Surface Resistivity
|
Ohm
|
ASTM-D-257
|
10 12
|
10 12
|
10 12
|
10 12
|
|
3
|
Volume Resistivity
|
Ohm cm
|
ASTM-D-257
|
10 16
|
10 16
|
10 16
|
10 16
|
|
4
|
Dielectric Constant
|
--
|
ASTM-D-150
|
2.8 to 4
|
|
5
|
Permittivity
23°C,50Hz
23°C,1kHz
23°C,10kHz
0°C,50Hz
50°C,50Hz
100°C,50 Hz
150°C,50Hz
|
--
|
IEC 250
|
3.26
3.24
3.21
3.26
3.27
3.35
3.65 |
| |
Dissipation Factor
23°C,50Hz
23°C,1kHz
23°C,10kHz
0°C,50Hz
50°C,50Hz
100°C,50 Hz
150°C,50Hz
|
--
|
IEC 250
|
0.002
0.0055
0.011
0.004
0.0015
0.007
0.006
|
| Chemical
Resistance |
| |
Dilute Acids & Alkalis
Concentrated Alkalis
Concentrated Hydrochloric Acid
Concentrated Sulphuric Acid
Greases,Oils & Fats
Organic Solvents,Alcohols, & Hydrocarbons
Ketones,Esters & Chlorinated Compounds
Phenols,Cresols & Chlorinated Phenols.
|
Good
Poor
Fair
Poor
Good
Good
Fairly Good
Poor
|
| Roll |
|
1
|
Width - Max
|
mm |
GPL method
|
1850
|
1850
|
1850
|
1525
|
|
2
|
Standard Length - Min
|
Mtrs
|
GPL Method
|
300
|
200
|
150
|
110
|
|
3
|
Standard Length - Max
|
Mtrs
|
GPL Method
|
2400
|
1600
|
1200
|
880
|
| Pancake |
|
1
|
Width - Min
|
mm
|
GPL Mehtod
|
11
|
11
|
11
|
11
|
|
2
|
Width - Max
|
mm |
GPL Method
|
150
|
150
|
150
|
150
|
|
3
|
Standard Length - Min
|
Mtrs
|
GPL Method
|
300
|
200
|
150
|
110
|
|
4
|
Standard Length - Max
|
Mtrs
|
GPL Method
|
1200
|
800
|
600
|
440
|
Garfilm EM 6 is
a Milky White Film specially developed as an insulating material
for rotating electrical machines, exhibits superior thermal ageing
performance compared to normal polyester films.